The effect of etching on glass polyalkenoate cements

The effect of acid etching on the surface appearance and flexural strength of four glass polyalkenoate cements was investigated. Specimens were etched for intervals of 10-60 s, both at the recommended time after mixing and after a 24-h delay. The surface texture was examined microscopically. Further specimens were subjected to a 4-point bend test following etching 1 h and 24 h after mixing. Deterioration of the surface appearance occurred as the etching time was increased beyond 10 s following immediate etching. Etching after 24 h reduced surface damage, but a 10-s etch still gave the most favourable surface appearance without loss of particulate material. Etching beyond 10 s significantly reduces flexural strength.