Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation
08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

Flowability of composites is no guarantee for contraction stress reduction

Milena Cadenaro1, Giulio Marchesi, Francesca Antoniolli

  • 1Department of Biomedicine, Unit of Dental Sciences and Biomaterials, University of Trieste, Via Stuparich, 1, I-34125 Trieste, Italy. m.cadenaro@fmc.units.it

Dental Materials : Official Publication of the Academy of Dental Materials
|January 13, 2009
PubMed
Abstract

More Related Videos

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials05:30

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

Published on: January 10, 2025

Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes09:41

Magnet Assisted Composite Manufacturing: A Flexible New Technique for Achieving High Consolidation Pressure in Vacuum Bag/Lay-Up Processes

Published on: May 17, 2018

Related Concept Videos

Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.
Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller width...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...