Composite chitosan/nano-hydroxyapatite scaffolds induce osteocalcin production by osteoblasts in vitro and support...

There is a significant clinical need to develop alternatives to autografts and allografts for bone grafting procedures. Porous, biodegradable scaffolds based on the biopolymer chitosan have been investigated as bone graft substitutes, and the addition of calcium phosphate to these scaffolds has been shown to improve the mechanical properties of the scaffold and may increase osteoconductivity. In this study, in vitro mineralization was examined for osteoblasts seeded in a porous scaffold composed of fused chitosan/nano-hydroxyapatite microspheres. Human fetal osteoblasts were cultured on composite and chitosan scaffolds for 21 days. On days 1, 4, 7, 14, and 21, total dsDNA, alkaline phosphatase, type I collagen, and osteocalcin production were measured. Total cellularity (measured by dsDNA), alkaline phosphatase, and type I collagen production were similar between the two scaffold groups. However, osteocalcin production occurred significantly earlier (day 7 vs. day 21) and was more than three times greater (0.0022 vs. 0.0068 ng/mL/ng DNA) on day 21 when osteoblasts were cultured on composite scaffolds. Osteocalcin is a marker of late osteoblastic differentiation and mineralized bone matrix formation. Therefore, the increase in osteocalcin production seen when cells were cultured on composite scaffolds may indicate that these scaffolds were superior to chitosan-only scaffolds in facilitating osteoblast mineralization. Composite scaffolds were also shown to be biocompatible and osteoconductive in a preliminary critical size rat calvarial defect study. These results demonstrate the potential of composite chitosan/nano-hydroxyapatite scaffolds to be used in bone tissue engineering.