Systematic error in mechanical measures of damage during four-point bending fatigue of cortical bone

Accumulation of fatigue microdamage in cortical bone specimens is commonly measured by a modulus or stiffness degradation after normalizing tissue heterogeneity by the initial modulus or stiffness of each specimen measured during a preloading step. In the first experiment, the initial specimen modulus defined using linear elastic beam theory (LEBT) was shown to be nonlinearly dependent on the preload level, which subsequently caused systematic error in the amount and rate of damage accumulation measured by the LEBT modulus degradation. Therefore, the secant modulus is recommended for measurements of the initial specimen modulus during preloading. In the second experiment, different measures of mechanical degradation were directly compared and shown to result in widely varying estimates of damage accumulation during fatigue. After loading to 400,000 cycles, the normalized LEBT modulus decreased by 26% and the creep strain ratio decreased by 58%, but the normalized secant modulus experienced no degradation and histology revealed no significant differences in microcrack density. The LEBT modulus was shown to include the combined effect of both elastic (recovered) and creep (accumulated) strain. Therefore, at minimum, both the secant modulus and creep should be measured throughout a test to most accurately indicate damage accumulation and account for different damage mechanisms. Histology revealed indentation of tissue adjacent to roller supports, with significant sub-surface damage beneath large indentations, accounting for 22% of the creep strain on average. The indentation of roller supports resulted in inflated measures of the LEBT modulus degradation and creep. The results of this study suggest that investigations of fatigue microdamage in cortical bone should avoid the use of four-point bending unless no other option is possible.