Parallel and orthogonal E-field alignment of single-walled carbon nanotubes by ac dielectrophoresis

We designed planar electrodes, for dielectrophoretic manipulation of single-walled carbon nanotubes (SWNTs), built as metal-oxide-semiconductor nanogap capacitors with common substrate and oxide thicknesses of 17 and 150 nm. Such design generates high electric fields (10(9) V m(-1)) and also the fringing field is curved due to the conducting substrate, unlike fields generated by conventionally used planar electrodes. Scanning electron microscopy images showed SWNTs aligned parallel and perpendicular to the electrodes. Raman spectroscopic mapping was used to produce separate images of the metallic (m-SWNT) and semiconducting (s-SWNT) nanotube density distributions. As expected, parallel alignment of the m-SWNTs with the E-field was found; however, also a perpendicular alignment of s-SWNTs was observed. Such orthogonal alignment of s-SWNTs is a rare observation and has not been experimentally reported before in detail with Raman images. Due to the unique electrode design, we were able to obtain substantial separation of m-SWNTs and s-SWNTs. Numerical modeling of the electric field factor of the dielectrophoresis force was done, and it matched perfectly with the experimental results. The orthogonal alignment of s-SWNTs results from comparable values of parallel and perpendicular polarizability to the nanotube axis.