CO2 Laser (10.6 microm) parameters for caries prevention in dental enamel

Although CO(2) laser irradiation can decrease enamel demineralisation, it has still not been clarified which laser wavelength and which irradiation conditions represent the optimum parameters for application as preventive treatment. The aim of the present explorative study was to find low-fluence CO(2) laser (lambda = 10.6 microm) parameters resulting in a maximum caries-preventive effect with the least thermal damage. Different laser parameters were systematically evaluated in 3 steps. In the first experiment, 5 fluences of 0.1, 0.3, 0.4, 0.5 and 0.6 J/cm(2), combined with high repetition rates and 10 micros pulse duration, were chosen for the experiments. In a second experiment, the influence of different pulse durations (5, 10, 20, 30 and 50 micros) on the demineralisation of dental enamel was assessed. Finally, 3 different irradiation times (2, 5 and 9 s) were tested in a third experiment. In total, 276 bovine enamel blocks were used for the experiments. An 8-day pH-cycling regime was performed after the laser treatment. Demineralisation was assessed by lesion depth measurements with a polarised light microscope, and morphological changes were assessed with a scanning electron microscope. Irradiation with 0.3 J/cm(2), 5 micros, 226 Hz for 9 s (2,036 overlapping pulses) increased caries resistance by up to 81% compared to the control and was even significantly better than fluoride application (25%, p < 0.0001). Scanning electron microscopy examination did not reveal any obvious damage caused by the laser irradiation.