Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives
Published on: May 17, 2020
Bond strength of self-etch adhesives to pre-etched enamel
Robert L Erickson1, Wayne W Barkmeier, Nicole S Kimmes
1Department of General Dentistry, Creighton University School of Dentistry, Omaha, NE 68178, USA.
Objective:
Bond strengths of composite resin to enamel using four self-etch adhesive (SEA) systems were compared with the bond strength of an etch-and-rinse adhesive (ERA) system, for both polished enamel and enamel pre-etched with phosphoric acid. The objective was to determine if the pre-etching would increase the bond strengths of the SEA systems to match the ERA system.
Methods:
Ten specimens were used for each adhesive to determine 24-h resin composite to enamel shear bond strengths (SBS) to polished (4000 grit) human enamel and this was repeated for the SEA systems for enamel that was pre-etched with phosphoric acid for 15s. SEM analysis was made to assess the degree of etching and resin penetration into enamel for each of the adhesive systems. Data were analyzed by a two factor ANOVA with a Tukey HSD post hoc test.
Results:
The SBS to polished enamel for all four SEA systems were statistically significantly lower (p<0.05) than the ERA control, but with pre-etched enamel there were no statistically significant differences (p>0.05) between any of the adhesive systems. All four of the SEA systems demonstrated statistically significant increases in bond strength between bonding to polished and pre-etched enamel, ranging from 27% to 86%. The results of SEM analysis showed no differences in the resin penetration patterns of any of the adhesives for enamel that was etched with phosphoric acid.
Significance:
Pre-etching enamel may enhance the bond strength of SEA systems to values comparable with those found with ERA adhesive systems, which may improve their overall performance in clinical use.
Related Concept Videos
01:12Bonding and Strength of Aggregate
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:09EDTA: Conditional Formation Constant
For the equilibrium reaction of the metal with the Y4− form of EDTA, the formation...
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons from...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...