Zn(5)Sb(4)In(2-delta) - a ternary derivative of thermoelectric zinc antimonides
Yang Wu1, Sven Lidin, Thomas L Groy
1Department of Chemistry and Biochemistry, Arizona State University, Tempe, Arizona 85287-1604, USA.
Abstract:
Zn(5)Sb(4)In(2-delta) (delta = 0.15(3)) was synthesized in the form of millimeter-sized crystals from reaction mixtures containing excess zinc. The ternary intermetallic compound is temperature polymorphic, and at room temperature it crystallizes with a new structure type in the orthorhombic space group Pbcn, where a = 7.1619(2), b = 17.1562(4), c = 8.6887(4) A, V = 1067.6(1) A(3), and Z = 4. The structure features 3(2)434 nets of Sb atoms that are stacked in antiposition to yield layers of square antiprisms sharing edges plus intervening tetracapped tetrahedra (tetreadersterns). The majority of Zn atoms occupy peripheral tetrahedra of such tetraedersterns, and attain at the same time the peculiar five-coordination by one like atom and four Sb atoms typical for the structures of binary zinc antimonides. The In and remaining Zn atoms are distributed in the tetragonal channels formed by the square antiprisms and display some disorder. At temperatures below 200 K Zn(5)Sb(4)In(2-delta) undergoes a phase transition into a more ordered structure with monoclinic symmetry (P2(1)/c) without any change of the unit cell. The thermoelectric properties of Zn(5)Sb(4)In(2-delta) were measured between 10 and 350 K. Exceptionally low thermal conductivity values (1 W/mK range) were obtained in the whole temperature range. Resistivity and thermopower values are characteristic of a heavily doped or degenerate semiconductor (2.5 mOmega cm and 160 muV/K, respectively, at room temperature) and show a discontinuity around 220 K. The thermoelectric figure of merit of Zn(5)Sb(4)In(2-delta) is higher than that of Zn(4)Sb(3) in the investigated temperature range.
Related Concept Videos
01:24Electrochemical Systems
02:49Calculating Standard Free Energy Changes
02:59The Nernst Equation
The interconnection between standard cell potentials and various thermodynamic parameters such as the standard free energy change ΔG° and equilibrium constant K has been previously explored. For example, a redox reaction involving zinc(II) and tin(II) ions at 1 M concentration with Eºcell = +0.291 V and ΔG° = −56.2 kJ is spontaneous.
02:46Crystal Field Theory - Tetrahedral and Square Planar Complexes
Crystal field theory (CFT) is applicable to molecules in geometries other than octahedral. In octahedral complexes, the lobes of the dx2−y2 and dz2 orbitals point directly at the ligands. For tetrahedral complexes, the d orbitals remain in place, but with only four ligands located between the axes. None of the orbitals points directly at the tetrahedral ligands. However, the dx2−y2 and dz2 orbitals (along the Cartesian axes) overlap with the ligands less than the dxy,...
01:26Imperfections in Crystal Structure: Stoichiometric Point Defects
02:42Ionic Crystal Structures
Most monatomic ions behave as charged spheres, and their attraction for ions of opposite charge is the same in every direction. Consequently, stable structures for ionic compounds result (1) when ions of one charge are surrounded by as many ions as possible of the opposite...