Gamma radiation alters the ultrastructure in tissue-engineered heart valve scaffolds

Xenogenic extracellular heart valve matrices have been suggested as scaffolds for tissue engineering. However, these matrices are immunogenic and stimulate an intense cell-mediated immune response and calcification. Mitigating the immunogenicity was attempted by different doses of gamma irradiation.

Mechanical properties of gamma-irradiated porcine matrices and control matrices (nonirradiated) were examined by tensile strength testing. Irradiated matrices (1, 10, 50, and 100 gray [Gy]) and control matrices were implanted subcutaneously in Wistar rats (n = 20). After 24 h, 1, 2, 3, and 4 weeks the explants were examined by light microscopy and transmission electron microscopy. Calcium (Ca) content was determined using inductively coupled plasma-mass spectrometry. Antibody reaction against porcine tissue in the rat serum was determined.

Tensile strength increased in irradiated matrices at the expense of elasticity. Ten gray-irradiated leaflets showed minimal lymphocytic inflammatory infiltration with preservation of ultrastructure. Ca levels after 2 weeks were as follows: control (0 Gy), 388 +/- 264 microg/mg; 1 Gy, 240 +/- 95 microg/mg; 10 Gy, 188 +/- 54 microg/mg; 50 Gy, 289 +/- 94 microg/mg; 100 Gy, 651 +/- 57 microg/mg. All implants still elicit an antibody immunoglobulin G reaction.

Exposure to 10 Gy gamma irradiation reduces lymphocytic inflammatory infiltrates and Ca levels in acellular porcine matrices with preservation of structural integrity. This could prolong the durability of these matrices.