Immobilization of alkaline phosphatase on microporous nanofibrous fibrin scaffolds for bone tissue engineering

Alkaline phosphatase (ALP) promotes bone formation by degrading inorganic pyrophosphate (PP(i)), an inhibitor of hydroxyapatite formation, and generating inorganic phosphate (P(i)), an inducer of hydroxyapatite formation. P(i) is a crucial molecule in differentiation and mineralization of osteoblasts. In this study, a method to immobilize ALP on fibrin scaffolds with tightly controllable pore size and pore interconnection was developed, and the biological properties of these scaffolds were characterized both in vitro and in vivo. Microporous, nanofibrous fibrin scaffolds (FS) were fabricated using a sphere-templating method. ALP was covalently immobilized on the fibrin scaffolds using 1-ethyl-3-(dimethylaminopropyl)carbodiimide hydrochloride (EDC). Scanning electron microscopic observation (SEM) showed that mineral was deposited on immobilized alkaline phosphatase fibrin scaffolds (immobilized ALP/FS) when incubated in medium supplemented with beta-glycerophosphate, suggesting that the immobilized ALP was active. Primary calvarial cells attached, spread and formed multiple layers on the surface of the scaffolds. Mineral deposition was also observed when calvarial cells were seeded on immobilized ALP/FS. Furthermore, cells seeded on immobilized ALP/FS exhibited higher osteoblast marker gene expression compared to control FS. Upon implantation in mouse calvarial defects, both the immobilized ALP/FS and FS alone treated group had higher bone volume in the defect compared to the empty defect control. Furthermore, bone formation in the immobilized ALP/FS treated group was statistically significant compared to FS alone group. However, the response was not robust.