Related Experiment Video

Updated: Jun 22, 2026

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way
07:42

Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way

Published on: November 21, 2017

Long-term leaching test of organo-contaminated cement-clay pastes

L Zampori1, P Gallo Stampino, G Dotelli

  • 1Dipartimento di Chimica, Materiali e Ingegneria Chimica 'G.Natta', INSTM R.U.-Politecnico di Milano, Piazza L. da Vinci 32, 20133 Milano, Italy.

Journal of Hazardous Materials
|June 16, 2009
PubMed

More Related Videos

A Protocol for Collecting and Constructing Soil Core Lysimeters13:23

A Protocol for Collecting and Constructing Soil Core Lysimeters

Published on: June 6, 2016

Design and Construction of an Experimental Setup to Enhance Mineral Weathering through the Activity of Soil Organisms07:22

Design and Construction of an Experimental Setup to Enhance Mineral Weathering through the Activity of Soil Organisms

Published on: November 10, 2023

Related Concept Videos

Microbial Leaching01:27

Microbial Leaching

Microbial leaching, also known as bioleaching, is an environmentally favorable method for extracting metals from low-grade ores using specific microorganisms. This biotechnological approach is particularly valuable for mining operations targeting copper, gold, and uranium, where traditional extraction methods may be economically or environmentally impractical.Copper Leaching and Microbial CatalysisIn copper bioleaching, crushed ore is arranged into heaps and irrigated with a dilute sulfuric...
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
Testing Water Quality01:14

Testing Water Quality

When the quality of water for concrete preparation is uncertain, its impact on the setting time of cement and compressive strength of mortar is assessed by comparison with de-ionized or distilled water benchmarks. American Society for Testing and Materials (ASTM) C1602 requires the setting times to be within 90 minutes of the control, British Standard (BS) 3146:1980 allows a 30-minute variance in the initial setting, while British Standards European Norm (BS EN) 1008 specifies initial setting...
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is critical—it...
Deleterious Substances in Aggregate01:25

Deleterious Substances in Aggregate

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...