Raman gain measurements and photo-induced transmission effects of germanium- and arsenic-based chalcogenide glasses

The Raman gain spectra of millimeter thick As(2)S(3) and As(24)S(38)Se(38) glasses and Ge((23 - x))Ga(x)Sb(7)S((70 - y))Se(y) with x = 0 and 5 and y = 0, 2, 5 have been measured using a direct nonlinear optics technique. The pump light originated from a picosecond Nd:YAG laser operating at 1064 nm and a tunable optical parametric generator and amplifier (OPG/OPA) was used as a source for the probe light. A peak material Raman gain coefficient of (155 +/- 11) x 10(-13) m/W has been measured for the As(24)S(38)Se(38) glass. A reversible photodarkening effect which responds to picosecond pulses is also reported. Finally, surface optical damage threshold measurements were found to be less than 9 GW/cm(2) for the reported samples, values which are comparable to some TeO(2)-based glasses with lower nonlinearities.