Particle size distribution, concentration, and magnetic attraction affect transport of polymer-modified Fe(0)...

The effect of particle concentration, size distribution (polydispersity) and magnetic attractive forces (Fe(0) content) on agglomeration and transport of poly(styrene sulfonate) (PSS) modified NZVI was studied in water-saturated sand (d(p) = 300 microm) columns. Particle concentrations ranged from 0.03 to 6 g/L in 5 mM NaCl/5 mM NaHCO3 at a pore water velocity of 3.2 x 10(-4) m/s. Three NZVI dispersions with different intrinsic particle size distributions obtained from sequential sedimentation are compared. The influence of magnetic attraction (Fe(0) content) on NZVI agglomeration and deposition in porous media is assessed by comparing the deposition behavior of PSS-modified NZVI (magnetic) having different Fe(0) contents with PSS-modified hematite (nonmagnetic) with the same surface modifier. At low particle concentration (30 mg/L) all particles were mobile in sand columns regardless of size or magnetic attractive forces. At high concentration (1 to 6 g/L), deposition of the relatively monodisperse dispersion containing PSS-modified NZVI (hydrodynamic radius (R(H)) = 24 nm) with the lowest Fe(0) content (4 wt%) is low (attachment efficiency (alpha) = 2.5 x 10(-3)), insensitive to particle concentration, and similar to PSS-modified hematite. At 1 to 6 g/L, the attachment efficiency of polydisperse dispersions containing both primary particles and sintered aggregates (R(H) from 15 to 260 nm) of PSS-modified NZVI with a range of Fe(0) content (10-60%) is greater (alpha = 1.2 x 10(-2) to 7.2 x 10(-2) and is sensitive to particle size distribution. The greater attachment for larger, more polydisperse Fe(0) nanoparticles with higher Fe(0) content is a result of their agglomeration during transport in porous media because the magnetic attractive force between particles increases with the sixth power of particle/agglomerate radius. A filtration model that considers agglomeration in porous media and subsequent deposition explains the observed transport of polydisperse PSS-modified NZVI at high concentration.