Hybrid organic-inorganic silica monolith with hydrophobic/strong cation-exchange functional groups as a sorbent for...

A hybrid organic-inorganic silica monolith with hydrophobic and strong cation-exchange functional groups was prepared and used as a sorbent for micro-solid phase extraction (micro-SPE). The hybrid silica monolith functionalized with octyl and thiol groups was conveniently synthesized by hydrolysis and polycondensation of a mixture of tetraethoxysilane (TEOS), n-octyltriethoxysilane (C8-TEOS) and 3-mercaptopropyltrimethoxysilane (MPTMS) via a two-step catalytic sol-gel process. Due to the favorable chemical reactivity of mercapto pendant moieties, the obtained hybrid monolith was oxidized using hydrogen peroxide (30%, w/w) to yield sulfonic acid groups, which provided strong cation-exchange sites. The obtained hybrid monolith was characterized by diffused infrared spectroscopy, elemental analysis, scanning electron microscopy and mercury intrusion porosimetry. The results show that the resulting monolith contains much higher carbon (31.6%) and sulfur (4.8%) contents than traditionally bonded silica materials. The extraction performance of the hybrid monolith was evaluated using sulfonamides as testing analytes by micro-SPE on-line coupled to HPLC. The results show that the hybrid monolith with hydrophobic and strong cation-exchange functional groups exhibits high extraction efficiency towards the testing analytes. The column-to-column RSD values were 1.3-9.8% for the extraction of SAs investigated. The extraction performance of the hybrid silica monolith remained practically unchanged after treated with acid (pH 1.0) and basic solutions (pH 10.5). Finally, the application of the hybrid monolith was demonstrated by micro-SPE of sulfonamide residues from milk followed by HPLC-UV analysis. The limits of detection (S/N=3) for eight SAs were found to be 1.0-3.0ng/mL in milk. The recoveries of eight SAs spiked in milk sample ranged from 80.2% to 115.6%, with relative standard deviations less than 11.8%.