Microleakage of ceramic inlays luted with different resin cements and dentin adhesives
Bulent Uludag1, Ozge Ozturk, A Nilgun Ozturk
1Department of Prosthodontics, University of Ankara, Faculty of Dentistry, Gazi University, Ankara, Turkey. bculudag@gmail.com
Statement Of Problem:
Despite recent advances in adhesive dentistry, resin cement/dentin adhesive combinations are not able to prevent microleakage in ceramic inlays. Marginal quality of tooth-colored restorations in large Class II cavities is satisfactory in enamel margins, but microleakage in dentin margins remains a concern.
Purpose:
The purpose of this study was to evaluate the microleakage of all-ceramic inlays luted with 2 dual-polymerizing resin cements or 1 autopolymerizing resin cement in combination with different dentin adhesives.
Material And Methods:
One hundred and twenty extracted human mandibular third molars were used in this study. Teeth were prepared to receive Class II MOD inlays with enamel gingival margins on 1 proximal surface and dentin gingival margins on the other surface. One hundred and twenty prepared teeth were divided into 3 groups of 40; 1 group for each resin cement: RelyX ARC, Variolink II, or Panavia 21. Each of the 3 groups were further divided into 4 dentin adhesive groups; Single Bond, ExciTE DSC, ED Primer, or Admira Bond. Each of the resin cements were used in combination with the 4 dentin adhesives, and IPS Empress ceramic inlays were placed with 12 different cement/adhesive combinations. After 1000 thermal cycles in a 5 degrees -55 degrees C water bath with a dwell time of 30 seconds, all specimens were subjected to cyclic axial mechanical loading. Then the restored teeth were stored in 0.5% basic fuchsin solution for 24 hours. The extent of dye penetration along the margins was measured with a stereomicroscope at x40 magnification. The data were evaluated statistically using repeated-measures ANOVA and Duncan tests (alpha=.05).
Results:
Microleakage at dentin margins was greater than that at enamel margins (P<.05) for all groups. Variolink II and RelyX ARC resin cements showed significantly lower microleakage results than Panavia 21 with all dentin adhesives in enamel margins. For dentin margins, Variolink II/Admira Bond combination showed the lowest microleakage value in dentin (P<.05).
Conclusions:
The overall microleakage at the enamel margins was significantly less than at the dentin margins (P<.05). Panavia 21 showed higher microleakage values than Variolink II and RelyX ARC in enamel margins.