A molecular dynamics simulation study of LiFePO4/electrolyte interfaces: structure and Li+ transport in carbonate and...

We have performed atomistic molecular dynamics (MD) simulations of the (010) surface of LiFePO(4) in contact with an organic liquid electrolyte (OLE), ethylene carbonate : dimethyl carbonate (3 : 7) with approximately 1 mol kg(-1) LiPF(6), and an ionic liquid-based electrolyte (ILE), 1-ethyl 3-methyl-imidazolium: bis(fluorosulfonyl)imide (EMIM(+) : FSI(-)) with approximately 1 mol kg(-1) LiFSI. Surface-induced structure that extends about 1 nm from the LiFePO(4) surface was observed in both electrolytes. The electrostatic potential at the LiFePO(4) surface was found to be negative relative to the bulk electrolyte reflecting an excess of negative charge from the electrolyte coordinating surface Li(+). In the ILE system negative surface charge is partially offset by a high density of EMIM(+) cations coordinating surface oxygen. The electrostatic potential exhibits a (positive) maximum about 3 A from the LiFePO(4) surface which, when combined with the reduced ability of the highly structured electrolytes to solvate Li(+) cations, results in a free energy barrier of almost 4 kcal mol(-1) for penetration of the interfacial electrolyte layer by Li(+). The resistance for bringing Li(+) from the bulk electrolyte to the LiFePO(4) surface through this interfacial barrier was found to be small for both the OLE and ILE. However, we find that the ability of EMIM(+) cations to donate positive charge to LiFePO(4)/electrolyte interface may result in a significant decrease in the concentration of Li(+) at the surface and a corresponding increase in impedance to Li(+) intercalation into LiFePO(4), particularly at lower temperatures.