In vivo comparison of near infrared lasers for skin welding

The skin closure abilities of near infrared lasers and suturing were compared by histological examination and mechanical tensile tests during a 21-day healing period. One-centimeter incisions on the dorsal skin of Wistar rats were treated by one of the closing techniques: (a) soldering, using an 809 nm diode laser (0.5 W, 5 s) with 25% bovine serum albumin (BSA) and 2.5 mg/ml indocyanine green (ICG); (b) direct welding with a 980 nm diode laser (0.5 W, 5 s); (c) direct welding with a 1,070 nm fiber laser (0.5 W, 5 s); (d) suturing. Six spots (79.61 J/cm(2) for each spot) were applied through the incisions. Healing was inspected on the 1st, 4th, 7th, 14th, and 21st post-operative days. The closure index (CI), thermally altered area (TAA), granulation area (GA) and epidermal thickness (ET) were determined by histological examination. Tensile tests were performed at a 5 mm/min crosshead speed up to the first opening along the incision. Immediate superficial closure with high CI values was found for the laser-irradiated incisions at the early phase of recovery. Clear welds without thermal damage were observed for the group irradiated at 1,070 nm. For the sutured group, the incisions remained unclosed for the first day, and openings through the incision were observed. At the end of the 21-day recovery period, no differences between experimental groups were observed in terms of the CI, GA and ET values. However, the tensile strength of the groups irradiated at 980 nm and 1,070 nm was found to be higher than that of the sutured incisions. The laser welding techniques were found to be reliable in terms of immediate and mechanically strong closure compared with suturing. Of them, 1,070 nm laser welding yielded noticeably stronger bonds, with minimal scarring at the end of the 21-days of recovery.