A convenient solvothermal synthesis route to metal phosphides with a shape of hollow nanospheres
Keyan Bao1, Shuzhen Liu, Jie Cao
1Hefei National Laboratory for Physical Science at Microscale and Department of Chemistry, University of Science and Technology of China, Hefei, Anhui 230026, PR China.
Abstract:
InP hollow nanospheres with an average size of 550 nm and shell thickness of about 110 nm were solvothermally synthesized in EA (ethanolamine)-H2O binary solution at 190 degrees C for 36 h. The shells of InP hollow nanospheres were composed of small nanoparticles. The similar route has been extended to prepare Cd3P2, Cu3P and Sn4P3 hollow nanospheres in 150-190 degrees C for 24-36 h.
More Related Videos
07:14Experimental Approaches for the Synthesis of Low-Valent Metal-Organic Frameworks from Multitopic Phosphine Linkers
Published on: May 12, 2023
![The Synthesis of [Sn10(Si(SiMe3)3)4]2- Using a Metastable Sn(I) Halide Solution Synthesized via a Co-condensation Technique](/_next/image?url=https%3A%2F%2Fcloudfront.jove.com%2FCDNSource%2Fteasers%2F54498.jpg&w=3840&q=50)
12:43The Synthesis of [Sn10(Si(SiMe3)3)4]2- Using a Metastable Sn(I) Halide Solution Synthesized via a Co-condensation Technique
Published on: November 28, 2016