Effect of fluoride-containing desensitizing agents on the bond strength of resin-based cements to dentin

Duygu Saraç1, Safak Külünk, Y Sinasi Saraç

  • 1Department of Prosthetic Dentistry, Faculty of Dentistry, Ondokuz May s University, Samsun, Turkey. dsarac@omu.edu.tr

Journal of Applied Oral Science : Revista FOB
|November 26, 2009
PubMed
Abstract

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Essential Minerals for Bone Health01:31

Essential Minerals for Bone Health

The minerals contained in all of the food we consume are essential for our organ systems. However, certain essential minerals, such as calcium, phosphorus, magnesium, manganese, and fluoride, largely affect bone health.
Calcium and Phosphorus
Calcium is a critical component of bones, especially in the form of calcium phosphate and calcium carbonate. Since the body cannot make calcium, it must be obtained from the diet. However, calcium cannot be absorbed from the small intestine without...
Solubility Equilibria: Overview01:09

Solubility Equilibria: Overview

When a substance such as sodium chloride is added to water, it dissolves, forming an aqueous solution. The extent of dissolution is called solubility. The process of dissolution can exist in equilibrium, just like other chemical processes. Solubility equilibria are also called precipitation equilibria because the process of solubility can be reversible. The reverse of the solubility process is called precipitation.
Solubility is important in biological and environmental processes. A notable...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...