Related Experiment Video

Updated: Jun 18, 2026

Development of Sulfidogenic Sludge from Marine Sediments and Trichloroethylene Reduction in an Upflow Anaerobic Sludge Blanket Reactor
15:19

Development of Sulfidogenic Sludge from Marine Sediments and Trichloroethylene Reduction in an Upflow Anaerobic Sludge Blanket Reactor

Published on: October 15, 2015

Hydrogen sulphide removal from corroding concrete: comparison between surface removal rates and biomass activity

H S Jensen1, A H Nielsen, P N L Lens

  • 1Department of Biotechnology, Chemistry and Environmental Engineering, Aalborg University, Aalborg, Denmark. hsj@bio.aau.dk

Environmental Technology
|December 3, 2009
PubMed

More Related Videos

Biogas Purification through the use of a Microalgae-Bacterial System in Semi-Industrial High Rate Algal Ponds07:34

Biogas Purification through the use of a Microalgae-Bacterial System in Semi-Industrial High Rate Algal Ponds

Published on: March 22, 2024

Evaluation of Integrated Anaerobic Digestion and Hydrothermal Carbonization for Bioenergy Production07:34

Evaluation of Integrated Anaerobic Digestion and Hydrothermal Carbonization for Bioenergy Production

Published on: June 15, 2014

Related Concept Videos

Microbial Bioremediation of Hydrocarbons01:26

Microbial Bioremediation of Hydrocarbons

Bioremediation is an environmentally sustainable process that employs living organisms—primarily microorganisms—to degrade or neutralize pollutants from contaminated environments. In oil spills and hydrocarbon pollution, bioremediation involves the use of hydrocarbon-degrading bacteria to transform toxic compounds into less harmful substances. This approach leverages natural microbial metabolic processes and is considered both cost-effective and ecologically favorable compared to physical or...
Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...
Bioremediation00:46

Bioremediation

Bioremediation is the use of prokaryotes, fungi, or plants to remove pollutants from the environment. This process has been used to remove harmful toxins in groundwater as a byproduct of agricultural run-off and also to clean up oil spills.
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Sulfate Attack on Concrete01:29

Sulfate Attack on Concrete

Sulfate attack on concrete is a deterioration process characterized by a whitish discoloration beginning at the edges and corners, accompanied by cracking and spalling. This phenomenon occurs when sulfates react with the components of hardened concrete, forming compounds like calcium sulfate and calcium sulfoaluminate which occupy more space than the substances they replace, causing the concrete to expand and disrupt.
Sulfates from sources like soil, groundwater, or industrial effluents...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...