Two-year water degradation of self-etching adhesives bonded to bur ground enamel

To evaluate the effect of water storage on the microshear bond strength to ground enamel of three "all-in-one" self-etch adhesives: Futurabond DC, Clearfil S Tri Bond and Hybrid bond; a self-etching primer; Clearfil SE Bond and an etch-and-rinse adhesive system, Admira Bond. Sixty human molars were used. The root of each tooth was removed and the crown was sectioned into two halves. The convex enamel surfaces were reduced by polishing on silicon paper to prepare a flat surface that was roughened with a parallel-sided diamond bur with abundant water for five seconds. The bonding systems were applied on this surface. Prior to adhesive curing, a hollow cylinder (2.0 mm in height/0.75 mm in internal diameter) was placed on the treated surfaces and cured. A resin composite was then inserted into the tube and cured. For each adhesive, two procedures were carried out: A--the specimens were kept in water for 24 hours, then the tube was removed and the microshear bond strength was determined in a universal testing machine at a crosshead speed of 0.5 mm/minute; B--the specimens were stored in water for two-years before microshear testing. The fractured surface of the bonded specimens after each test procedure was examined by SEM. For the 24-hour control, there was no significant difference in bond strength between the tested adhesives. After two years of water storage, the bond strength of Admira Bond, Clearfil SE Bond and Futurabond DC decreased, but the reduction was not significantly different from that of 24 hours. For Clearfil S Tri Bond and Hybrid Bond, the bond strengths were significantly reduced compared to their 24-hour results.