Binary Au/MWCNT and ternary Au/ZnO/MWCNT nanocomposites: synthesis, characterisation and catalytic performance

Gold nanoparticles of 10-24 and 5-8 nm in size were obtained by chemical citrate reduction and UV photoreduction, respectively, on acid-treated multiwalled carbon nanotubes (MWCNTs) and on ZnO/MWCNT composites. The shape and size of the deposited Au nanoparticles were found to be dependent upon the synthetic method used. Single-crystalline, hexagonal gold particles were produced in the case of UV photoreduction on ZnO/MWCNT, whereas spherical Au particles were deposited on MWCNT when the chemical citrate reduction method was used. In the UV photoreduction route, n-doped ZnO serves as the e(-) donor, whereas the solvent is the hole trap. All materials were fully characterised by UV/Vis spectroscopy, scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, Raman spectroscopy and BET surface analysis. The catalytic activity of the composites was studied for the selective hydrogenation of alpha,beta-unsaturated carbonyl compound 3,7-dimethyl-2,6-octadienal (citral). The Au/ZnO/MWCNT composite favours the formation of unsaturated alcohols (selectivity=50% at a citral conversion of 20%) due to the presence of single-crystalline, hexagonal gold particles, whereas saturated aldehyde formation is favoured in the case of the Au/MWCNT nanocomposite that contains spherical gold particles.