Optimization of nano-scale nickel/iron particles for the reduction of high concentration chlorinated aliphatic
Robert J Barnes1, Olga Riba, Murray N Gardner
1Department of Earth Sciences, University of Oxford, Parks Road, Oxford OX1 3PR, UK.
Abstract:
The use of nano-scale particles as a means of environmental remediation still provides a comparatively novel approach for the treatment of contaminated waters. The current study compares the reactivity of micro-scale Fe, nano-scale Fe and nano-scale Ni/Fe (nickel/iron) particles specifically for dechlorination of solutions containing 350 mg L(-1) of TCE (concentration measured at a contaminated site in Derbyshire, UK). The results indicated that employing 1 g L(-1) of reactive material for dechlorination in the monometallic form (both micro- and nano-scale) exhibited very little reduction capability compared with the bimetallic Ni/Fe nano-scale particles, containing 28.9% Ni (in molar), which achieved complete dechlorination of the TCE in solution within 576 h. Experiments were also performed to determine the optimum bimetallic composition of the Ni/Fe particles for TCE reduction. This revealed that 3.2% Ni was the optimum Ni/Fe molar ratio for both maximum dehalogenation performance and minimum release of Ni into solution. Using particles of the most effective bimetallic composition, experiments were carried out to determine the concentration required for optimal TCE reduction. Over the range of nano-scale particle concentrations tested (0.1-9 g L(-1)), reduction rates of TCE increased with greater TCE:nano-scale particle ratios. However, a concentration range of 1-3 g L(-1) was selected as the most appropriate for site remediation, since more concentrated solutions demonstrated only small increases in rates of reaction. Finally, in order to test the long term performance and reactivity of the 3.2% Ni/Fe bimetallic nano-scale particles, weekly spikes of 350 mg L(-1) TCE were injected into a 3 g L(-1) nano-scale particle batch reactor. Results showed that the bimetallic nano-scale particles had the ability to reduce 1750 mg L(-1) TCE and remained active for at least 13 weeks.
More Related Videos
08:13Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area
Published on: February 19, 2018
12:08Catalytic Reactions at Amine-Stabilized and Ligand-Free Platinum Nanoparticles Supported on Titania During Hydrogenation of Alkenes and Aldehydes
Published on: June 24, 2022
Related Concept Videos
02:17Reduction of Alkenes: Asymmetric Catalytic Hydrogenation
The metal catalyst used can be either heterogeneous or homogeneous. When hydrogenation of an alkene generates a chiral center, a pair of enantiomeric products is expected to form. However, an enantiomeric excess of one of the products can be facilitated using an enantioselective reaction or an...
01:03Precipitation Gravimetry
In determining nickel by gravimetric analysis, a precipitant of ethanolic dimethylglyoxime is added to a hot nickel salt solution. This is quickly followed by the dropwise addition of dilute ammonia solution until precipitation occurs. A...
02:13Reduction of Alkenes: Catalytic Hydrogenation
Metals like palladium, platinum, and nickel are commonly used in their solid forms — fine powder on an inert surface. As these catalysts remain insoluble in the reaction mixture, they are referred to as heterogeneous catalysts.
The hydrogenation process takes place on the surface of...
02:24Reduction of Alkynes to cis-Alkenes: Catalytic Hydrogenation
Like alkenes, alkynes can be reduced to alkanes in the presence of transition metal catalysts such as Pt, Pd, or Ni. The reaction involves two sequential syn additions of hydrogen via a cis-alkene intermediate.