Enhanced electroluminescence from SiN-based multilayer structure by laser crystallization of ultrathin amorphous...

Luminescent SiN-based multilayers were prepared in a plasma enhanced chemical vapor deposition system followed by subsequently laser crystallization of ultrathin amorphous Si-rich SiN sublayers. The cross-sectional TEM analysis reveals that grain size of Si nanocrystals embedded in the Si-rich SiN sublayers is independent of the laser fluence, while the grain density can be well controlled by the laser fluence. The devices containing the laser crystallized multilayers show a low turn-on voltage of 5 V and exhibit strong green light emission under both optical and electrical excitations. Moreover, the device after laser-irradiated at 554 mJ/cm(2) shows a significantly enhanced EL intensity as well as external quantum efficiency compared with the device without laser irradiation. The EL mechanism is suggested from the bipolar recombination of electron-hole pairs at Si nanocrystals. The improved performance of the devices was discussed.