Changes in surface morphology and mineralization level of human enamel following in-office bleaching with 35%...

The objective of this study was to evaluate the alterations on surface morphology and mineral loss of human enamel following in-office bleaching with 35% hydrogen peroxide and light irradiation. Dental enamel samples were obtained from human third molars and randomly divided into 10 groups (n = 10). The control group remained untreated. Bleached groups were treated with one of three whitening products. Bleaching was performed in a single session, during which bleaching gel was applied to the enamel surface three times for 10 minutes each time. During treatment, the bleaching agents were either irradiated by a halogen light or an LED/diode laser or were not irradiated at all. Microhardness testing was performed with a Knoop indentor and the surface morphologic observations were carried out by scanning electron microscopy (SEM). Cross-sectional microhardness (CSMH) and polarized light microscopy (PLM) were used to measure the depth of demineralization. The results revealed a significant decrease in surface microhardness values and changes to the enamel morphology after bleaching. CSMH and PLM showed that bleached enamel presented lower volume percentage of mineral up to 40 micrometers from the enamel surface and demineralization areas located in the subsuperficial region of enamel, respectively. It was concluded that 35% hydrogen peroxide can alter the surface morphology and the mineralization level of the dental enamel surface and sub-surface regardless of what type of bleaching light is used.