Related Experiment Video

Updated: Jun 15, 2026

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Resistance of composite and amalgam core foundations retained with and without pins and bonding agents

Terence A Imbery1, Ryan Swigert, Brian Richman

  • 1Department of General Practices, Virginia Commanwealth University, School of Dentistry, Richmond, VA, USA.

General Dentistry
|March 19, 2010
PubMed

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Reinforcements in Concrete01:25

Reinforcements in Concrete

Reinforced concrete is a composite material used extensively in construction, combining the compressive strength of concrete with the tensile strength of steel. This synergy is essential as concrete, while excellent at resisting compression, is weak under tension. Steel bars, or rebars, are embedded in the concrete to handle these tensile forces. The choice of steel is strategic; it shares a similar coefficient of thermal expansion with concrete, which ensures uniformity in response to...
Composite Masonry Walls01:18

Composite Masonry Walls

Composite masonry walls combine multiple wythes of the same or different masonry materials to create a unified structure. These walls feature wythes that are bonded together either through mortar-filled collar joints, grouted spaces, or more commonly, with rigid metal ties and reinforcements, with the use of masonry header units being rare. Metal ties are preferred because they effectively minimize water penetration, as these walls primarily absorb moisture and then release it into the...
Posttensioned Masonry Walls01:15

Posttensioned Masonry Walls


Post-tensioned masonry walls use high-strength steel rods or flexible tendons to enhance the strength and efficiency of masonry structures. These elements are securely anchored to the foundation and extend vertically either within the cores of the masonry units or between the masonry wythes. The construction process involves building the wall with these tensioning elements in place and allowing the mortar to fully cure.
Following the curing process, the tensioning begins. Steel rods are...
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...