High-contrast solid-state electrochromic devices of viologen-bridged polysilsesquioxane nanoparticles fabricated by...

Water-soluble silsesquioxane nanoparticles (NPs) incorporating viologen groups (PXV; 1,1'-bis[3-(trimethoxysilyl)propyl]-4,4'-bipyridinium iodide) have been synthesized by sol-gel polymerization. The electrochromic properties of the bulk film fabricated by layer-by-layer (LbL) assembly have been examined, along with their incorporation into solid-state devices. The orange LbL films show high thermal stability and exhibit a maximum UV-vis absorption at 550 nm. Electrochromic switching of the NPs in liquid electrolyte as well as in the solid state was evaluated by a kinetic study via measurement of the change in transmission (% T) at the maximum contrast. Cyclic voltammograms of the PXV NP LbL films exhibit a reversible reduction at -0.6 V vs Ag/AgCl in a 0.1 M NaClO4(aq) solution, revealing good electrochromic stability, with a color change from orange to dark purple-blue at applied potentials ranging from -0.7 to -1.3 V. Cathodically coloring PXV NP solid-state devices exhibit a switching time of a few seconds between the purple-blue reduced state and the orange oxidized state, showing a contrast of 50% at 550 nm and a coloration efficiency of 205 cm2/C. Their solubility and fairly fast electrochromic switching ( approximately 3 s) at low switching voltages (between 0 and 3.0 V), along with their stability under atmospheric conditions, make PXV NPs good candidates for electrochromic displays.