The influence of rotating fatigue on the bond strength of zirconia-composite interfaces

Hesam Mirmohammadi1, Moustafa N Aboushelib, Cornelis J Kleverlaan

  • 1Department of Dental Materials Science, Academic Centre of Dentistry Amsterdam (ACTA), Universiteit van Amsterdam and Vrije Universiteit, The Netherlands. hmirmoha@acta.nl

Dental Materials : Official Publication of the Academy of Dental Materials
|April 16, 2010
PubMed
Abstract

Keywords:
dental materials fatiguezirconia resin bondrotating fatigue testingcomposite interface strength

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
Transformation of Plane Stress01:18

Transformation of Plane Stress

Studying stress transformation is essential in understanding how stress components within a material, like a cube under plane stress, change with rotation. This change is analyzed by considering a prismatic element within the cube. As the element rotates, the stress components acting on it—both normal and shearing stresses—change in magnitude and orientation. This change is quantified using trigonometric functions of the rotation angle, relating the forces acting on the rotated element's faces...
Stress Concentrations in Circular Shafts01:18

Stress Concentrations in Circular Shafts

Consider the elastic torsion formula, which applies to a circular shaft with a consistent cross-section. This formula assumes that the shaft's ends are loaded with rigid plates firmly attached. However, in many cases, torques are applied to the shaft through mechanisms like flange couplings or gears, which are connected by keys inserted into keyways. This application method modifies the stress distribution near the point of torque application, causing it to deviate from the distributions...
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
Residual Stresses in Circular Shafts01:10

Residual Stresses in Circular Shafts

In materials that exhibit elastic and plastic behavior, known as elastoplastic materials, residual stresses can accumulate when these materials experience plastic deformation. This deformation arises from either high levels of shearing stress or significant strains. Residual stresses are internal stresses that persist within a material after removing the external force causing deformation. This phenomenon is demonstrated when observing the behavior of a shaft under torque; notably, the shaft's...