H(2) sensing characteristics of SnO(2) coated single wall carbon nanotube network sensors

SnO(2) nanoparticle coated single wall nanotube (SWNT) network sensors were fabricated by forming a SWNT network on the Pt patterned SiO(2)/Si substrate using a dip coating method and subsequently depositing SnO(2) nanoparticles on the SWNT network by rf magnetron sputtering. Their H(2) gas sensing properties were investigated. The SnO(2)-SWNT network sensors stably and reversibly responded to H(2) gas even at room temperature and could detect H(2) gas down to 100 ppm. In addition to the low temperature detection, a remarkable finding was that the gas sensing behavior of SnO(2)-SWNT network sensors was changed from p-type to n-type with increasing SnO(2) deposition time (i.e. surface coverage of SnO(2) on SWNT). A schematic model was proposed to explain the switching of sensing behavior depending on the surface coverage of SnO(2) nanoparticles on the SWNTs.