Structural evolution of Pd-doped nanoscale zero-valent iron (nZVI) in aqueous media and implications for particle...

Palladized zero-valent iron nanoparticles have been frequently employed to achieve enhanced treatment of halogenated organic compounds; however, no detailed study has been published on their structures, especially the location and distribution of palladium within the nanoparticles. In this work, the structural evolution of palladized nanoscale iron particles (Pd-nZVI, with 1.5 wt % Pd) was examined using X-ray photoelectron spectroscopy (XPS), scanning transmission electron microscopy (STEM), and X-ray energy dispersive spectroscopy (XEDS) techniques. The STEM-XEDS technique enables direct visualization of the nanoscale structural and compositional changes of the bimetallic particles. For a freshly made Pd-nZVI sample, the particles consist of a metallic iron core and a thin amorphous oxide shell, and Pd is observed to form 2-5 nm islands decorating the outer surface of the nanoparticles. Upon exposure to water, Pd-nZVI undergoes substantial morphological and structural changes. STEM-XEDS elemental maps show that Pd infiltrates through the oxide layer to the metallic iron interface, which is accompanied by oxidation and outward diffusion of the iron species. Within a 24 h period, Pd is completely buried underneath an extensive iron oxide matrix, and a fraction of the nanoparticles exhibits a hollowed-out morphology with no metallic iron remaining. The microstructural variations observed concur with the reactivity data, which shows that the aged bimetallic particles display an 80% decrease in dechlorination rate of trichloroethene (TCE) compared to that of the fresh particles. These findings shed new light on the function of palladium in hydrodechlorination reactions, nZVI aging and deactivation, and the longevity of Pd-nZVI nanoparticles for in situ remediation.