Effect on dynamic mechanical stability and interfragmentary movement of angle-stable locking of intramedullary nails...

Unstable distal tibia fractures are challenging injuries that require surgery. Increasingly, intramedullary nails are being used. However, fracture site anatomy may cause distal-fragment stabilization and fixation problems and lead to malunion/nonunion. We studied the influence of angle-stable nail locking on fracture gap movement and other biomechanical parameters.

Eight pairs of fresh human cadaver tibiae were used. The bone mineral density (BMD) was determined. All tibiae were nailed with a Synthes Expert tibial nail. Within each pair, one tibia was randomized to receive conventional locking screws; the other, angle-stable screws with sleeves. A 7-mm osteotomy was created 10 mm above the upper distal locking screw, to simulate an AO 42-A3 fracture. Biomechanical testing involved nondestructive mediolateral and anteroposterior pure bending, followed by cyclic combined axial and torsional loading to catastrophic failure. The neutral zone was determined. Fracture gap movement was monitored with 3-D motion tracking.

The angle-stable locked constructs had a significantly smaller mediolateral neutral zone (mean: 0.04 degree; p=0.039) and significantly smaller fracture gap angulation (p=0.043). The number of cycles to failure did not differ significantly between the locking configurations. BMD was a significant covariate affecting the number of cycles to failure (p=0.008). However, over the first 20,000 cycles, there was no significant correlation in the angle-stable construct.

Angle-stable locking of the Expert tibial nail was associated with a significant reduction in the mediolateral neutral zone and in fracture gap movement. Angle-stable fixation also reduced the influence of BMD over the first 20,000 cycles.