Selective extraction of CO2 from simulated flue gas using polymeric ionic liquid sorbent coatings in solid-phase...

The CO2 selectivity of two polymeric task-specific ionic liquid sorbent coatings, poly(1-vinyl-3-hexylimidazolium) bis[(trifluoromethyl)sulfonyl]imide [poly(VHIM-NTf2)] and poly(1-vinyl-3-hexylimidazolium) taurate [poly(VHIM-taurate)], was examined using solid-phase microextraction (SPME) for the determination of CO2 in simulated flue gas. For comparison purposes, a commercial SPME fiber, Carboxen-PDMS, was also studied. A study into the effect of humidity revealed that the poly(VHIM-taurate) fiber exhibited enhanced resistance to water, presumably due to the unique mechanism of CO2 capture. The effect of temperature on the performance of the PIL-based and Carboxen fibers was examined by generating calibration curves under various temperatures. The sensitivity, linearity, and linear range of the three fibers were evaluated. The extraction of CH4 and N2 was performed and the selectivities of the PIL-based and Carboxen fibers were compared. The poly(VHIM-NTf2) fiber was found to possess superior CO2/CH4 and CO2/N2 selectivities compared to the Carboxen fiber, despite the smaller film thicknesses of the PIL-based fibers. A scanning electron microscopy study suggests that the amine group of the poly(VHIM-taurate) is capable of selectively reacting with CO2 but not CH4 or N2, resulting in a significant surface morphology change of the sorbent coating.