3D Hydrogel Scaffolds for Articular Chondrocyte Culture and Cartilage Generation
Published on: October 7, 2015
Oxygen tension differentially regulates the functional properties of cartilaginous tissues engineered from
C T Buckley1, T Vinardell, D J Kelly
1Trinity Centre for Bioengineering, School of Engineering, Trinity College Dublin, Dublin 2, Ireland.
Background:
For current tissue engineering or regenerative medicine strategies, chondrocyte (CC)- or mesenchymal stem cell (MSC)-seeded constructs are typically cultured in normoxic conditions (20% oxygen). However, within the knee joint capsule a lower oxygen tension exists.
Objective:
The objective of this study was to investigate how CCs and infrapatellar fad pad derived MSCs will respond to a low oxygen (5%) environment in 3D agarose culture. Our hypothesis was that culture in a low oxygen environment (5%) will enhance the functional properties of cartilaginous tissues engineered using both cell sources.
Experimental Design:
Cell-encapsulated agarose hydrogel constructs (seeded with CCs or infrapatellar fat pad (IFP) derived MSCs) were prepared and cultured in a chemically defined serum-free medium in the presence (CCs and MSCs) or absence (CCs only) of transforming growth factor-beta3 (TGF-β3) in normoxic (20%) or low oxygen (5%) conditions for 42 days. Constructs were assessed at days 0, 21 and 42 in terms of mechanical properties, biochemical content and histologically.
Results:
Low oxygen tension (5%) was observed to promote extracellular matrix (ECM) production by CCs cultured in the absence of TGF-β3, but was inhibitory in the presence of TGF-β3. In contrast, a low oxygen tension enhanced chondrogenesis of IFP constructs in the presence of TGF-β3, leading to superior mechanical functionality compared to CCs cultured in identical conditions.
Conclusions:
Extrapolating the results of this study to the in vivo setting, it would appear that joint fat pad derived MSCs may possess a superior potential to generate a functional repair tissue in low oxygen tensions. However, in the context of in vitro cartilage tissue engineering, CCs maintained in normoxic conditions in the presence of TGF-β3 generate the most mechanically functional tissue.