Experimental friction coefficients for bovine cartilage measured with a pin-on-disk tribometer: testing configuration...

The friction coefficient between wet articular cartilage surfaces was measured using a pin-on-disk tribometer adopting different testing configurations: cartilage-on-pin vs. alumina-on-disk (CA); cartilage-on-pin vs. cartilage-on-disk (CC); and alumina-on-pin vs. cartilage-on-disk (AC). Several substances were dissolved in the phosphate buffered saline (PBS) solution to act as lubricants: 10,000 molecular weight (MW) polyethylene glycol (PEG), 100,000 MW PEG, and chondroitin sulfate (CS), all at 100 mg/mL concentration. Scanning electron microscopy photographs of the cartilage specimens revealed limited wear due to the experiment. Conducting the experiments in PBS solutions we provide evidence according to which a commercial pin-on-disk tribometer allows us to assess different lubrication mechanisms active in cartilage. Specifically, we find that the measured friction coefficient strongly depends on the testing configuration. Our results show that the friction coefficient measured under CC and AC testing configurations remains very low as the sliding distance increases, probably because during the pin displacement the pores present in the cartilage replenish with PBS solution. Under such conditions the fluid phase supports a large load fraction for long times. By systematically altering the composition of the PBS solution we demonstrate the importance of solution viscosity in determining the measured friction coefficient. Although the friction coefficient remains low under the AC testing configuration in PBS, 100 mg/mL solutions of both CS and 100,000 MW PEG in PBS further reduce the friction coefficient by ~40%. Relating the measured friction coefficient to the Hersey number, our results are consistent with a Stribeck curve, confirming that the friction coefficient of cartilage under the AC testing configuration depends on a combination of hydrodynamic, boundary, and weep bearing lubrication mechanisms.