Mechanical properties and in vitro bioactivity of Ca5(PO4)2SiO4 bioceramic

Pure Ca(5)(PO(4))(2)SiO(4) bioceramic was first prepared by a sol-gel method using triethyl phosphate, tetraethoxysilane, and calcium nitrate tetrahydrate as original materials. Simulated body fluid (SBF) immersion tests revealed that Ca(5)(PO(4))(2)SiO(4) samples had a greater in vitro apatite-forming ability than hydroxyapatite (HA). After soaking Ca(5)(PO(4))(2)SiO(4) samples in the SBF for 1 day, bone-like apatite precipitated on the surfaces and the apatite layer became thicker with increasing the soaking time. However, few bone-like apatites precipitated on the HA samples even after soaking in the SBF for 7 days. The good in vitro bioactivity of Ca(5)(PO(4))(2)SiO(4) samples was attributed to the silanol (Si-OH) groups and greater solubility of Ca(5)(PO(4))(2)SiO(4). In addition, hot-pressed Ca(5)(PO(4))(2)SiO(4) ceramic exhibited lower bending strength and elastic modulus than hot-pressed HA, since the former had a lower relative density than the latter. The results have shown that Ca(5)(PO(4))(2)SiO(4) is a potential candidate material for bone repair.