Effect of biofouling on anodized and sol-gel treated titanium surfaces: a comparative study

Anodization and sol-gel treatments of titanium (Ti) were evaluated as biofilm control measures on surfaces exposed to seawater exposed to ultraviolet light. Anodized and sol-gel treated specimens were characterized using Raman spectroscopy to confirm the presence of TiO(2). The single anatase phase was observed at the anodized surfaces whereas the anatase/rutile mixed phase was detected on the sol-gel coated surfaces. After exposure of the specimens to seawater, biofilms were characterized by total viable counts, and epifluorescence and Raman microscopy. These techniques confirmed the reduction in biofilm formation on both the anodized and sol-gel coated Ti specimens compared to the untreated specimens. Biofilm control by anodization was found to be more effective than by sol-gel treatment of the specimens. The higher particle size and the inhomogeneity at the sol-gel coated surfaces produced less effective biofilm control.