Degradation of polymeric restorative materials subjected to a high caries challenge

The aim of this study was to evaluate the degradation of different resin filling materials after a caries challenge, by high performance liquid chromatography (HPLC) and contact angle (θ) measurement.

Four different polymeric restorative materials (a resin composite, a polyacid-modified resin composite, an ormocer and a resin-modified glass ionomer cement) were tested. Five samples (30 mm × 6 mm × 2 mm) of each material were formed in a Teflon mold, following the manufacturer's instructions. After pH cycles, the solutions were injected in an HPLC. The θ was obtained, before and after pH cycle, by a goniometer at 60% air humidity and 25°C. A distilled water drop (0.006 ml) was put on the material surface, and after 6 min, 10 measures were obtained at 20s intervals. Each sample received 4 drops, one at a time, on different areas.

HPLC results showed elution of byproducts in all materials. This was greater in the acid medium. Bis-GMA and TEGDMA were detected in TPH Spectrum and Definite residues. Analyses of the contact angle by ANOVA and Student-Neuman-Keuls's test showed that the surfaces of TPH Spectrum, Dyract AP and Definite were altered, except Vitremer (p<0.05).

All materials tested degraded on a caries simulated medium, suggesting that a great effort should be made to disseminate oral health information, since a high caries challenge environment (low pH) can lead to dental composite degradation, with potential toxic risks to patients.