Corrosion behavior of Ti-5Ag alloy with and without thermal oxidation in artificial saliva solution

B B Zhang1, B L Wang, L Li

  • 1Center for Biomedical Materials and Engineering, Harbin Engineering University, Harbin 150001, China.

Dental Materials : Official Publication of the Academy of Dental Materials
|November 25, 2010
PubMed
Abstract

More Related Videos

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys07:12

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys

Published on: September 11, 2018

Imaging Corrosion at the Metal-Paint Interface Using Time-of-Flight Secondary Ion Mass Spectrometry07:24

Imaging Corrosion at the Metal-Paint Interface Using Time-of-Flight Secondary Ion Mass Spectrometry

Published on: May 6, 2019

Related Concept Videos

Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Oxidations of Aldehydes and Ketones to Carboxylic Acids01:15

Oxidations of Aldehydes and Ketones to Carboxylic Acids

Oxidation of aldehydes and ketones results in the formation of carboxylic acids. Aldehydes, bearing hydrogen next to the carbonyl group, are easily oxidized compared to ketones. This is because an aldehydic proton can easily be abstracted during oxidation.
Aldehydes readily undergo oxidation in strong oxidizing agents such as potassium permanganate and chromic acid. The oxidation can also be carried out using mild oxidizing agents such as silver oxide. In fact, aldehydes can be easily oxidized...