Effects of soldering and laser welding on bond strength of ceramic to metal
Akin Aladağ1, M Erhan Cömlekoğlu, Mine Dündar
1Department of Prosthodontics, School of Dentistry, University of Ege, Izmir, Turkey.
Statement Of Problem:
Welding or soldering of metal frameworks negatively affects the overall bond strength between the veneering ceramic and metal.
Purpose:
The purpose of this study was to evaluate the effect of soldering and laser-welding procedures on the bond strength between ceramic and metal.
Material And Methods:
Thirty Ni-based metal specimens (Wiron 99) (8 × 4 × 4 mm) were fabricated and divided into 3 groups; soldered (S), laser welded (L), and control (untreated cast alloy) (n=10). In S and L specimens, a notch (1 × 1.5 mm) was prepared longitudinally on the surface of each specimen and filled with compatible alloy (Wiron soldering rods and Wiroweld NC, respectively). Vickers hardness measurements were made after polishing the surfaces with a metallographic polishing kit. A veneering ceramic (VITA VMK 95) was vibrated, condensed in a mold, and fired on the metal frameworks. The specimens were sectioned in 2 axes to obtain nontrimmed bar specimens with a bonding area of approximately 1 mm². Forty bars per block were obtained. Each bar was subjected to microtensile bond strength (μTBS) testing with a crosshead speed of 1 mm/min. The μTBS data (MPa) were recorded, and SEM was used for failure analysis of the tested bars. The measurements were statistically analyzed using a 1-way ANOVA and Tamhane tests (α=.05).
Results:
The mean differences in μTBS of veneering ceramic to soldered (10.4 ±2.4 MPa) and laser-welded (11.7 ±1.3 MPa) metal surfaces were not significantly different and were significantly lower than that of the cast alloy (25.4 ±3.6 MPa) (P<.05). The mean Vickers hardness of cast alloy was significantly higher (236 ±17 HV) than soldered (114 ±9 HV) and laser-welded groups (129 ±11 HV) (P<.05).
Conclusions:
Soldering and laser welding significantly decreased the μTBS of a veneering ceramic to a base metal alloy.
Related Concept Videos
02:32Bonding in Metals
01:12Bonding and Strength of Aggregate
01:24Metal-Semiconductor Junctions
Schottky Barriers
Schottky barriers arise when a metal with a work function (Φm) contacts a semiconductor with a different work function (Φs). Initially, electrons transfer until the Fermi levels of the metal and semiconductor align at equilibrium. For instance, if Φm > Φs, the semiconductor Fermi level is higher than the metal's before contact. The semiconductor's...
01:27Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
01:17Steel Fastening Techniques
Rivets are cylindrical steel fasteners with a specially designed head. During application, rivets are heated until white-hot and then inserted through pre-drilled holes in the steel sections. A pneumatic hammer is used to shape the exposed end into a second head, securing the sections together.
Bolting is another...
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons from...