Cd(1-x)Zn(x)O [0.05 ≤x≤ 0.26] synthesized by vapor-diffusion induced hydrolysis and co-nucleation from aqueous metal salt solutions

Nanoparticulate Cd(1-x)Zn(x)O (x = 0, 0.05-0.26, 1) is synthesized in a simple two-step synthesis approach. Vapor-diffusion induced catalytic hydrolysis of two molecular precursors at low temperature induces co-nucleation and polycondensation to produce bimetallic layered hydroxide salts (M = Cd, Zn) as precursor materials which are subsequently converted to Cd(1-x)Zn(x)O at 400 °C. Unlike ternary materials prepared by standard co-precipitation procedures, all products presented here containing < 30 mol% Zn(2+) ions are homogeneous in elemental composition on the micrometre scale. This measured compositional homogeneity within the samples, as determined by energy dispersive spectroscopy and inductively coupled plasma spectroscopy, is a testimony to the kinetic control achieved by employing slow hydrolysis conditions. In agreement with this observation, the optical properties of the materials obey Vegard's Law for a homogeneous solid solution of Cd(1-x)Zn(x)O, where x corresponds to the values determined by inductively coupled plasma analysis, even though powder X-ray diffraction shows phase separation into a cubic mixed metal oxide phase and a hexagonal ZnO phase at all doping levels.