Fluoride adsorption studies on mixed-phase nano iron oxides prepared by surfactant mediation-precipitation technique

Mixed nano iron oxides powder containing goethite (α-FeOOH), hematite (α-Fe(2)O(3)) and ferrihydrite (Fe(5)HO(8)·4H(2)O) was synthesized through surfactant mediation-precipitation route using cetyltrimethyl ammonium bromide (CTAB). The X-ray diffraction, FTIR, TEM, Mössbauer spectroscopy were employed to characterize the sample. These studies confirmed the nano powder contained 77% goethite, 9% hematite and 14% ferrihydrite. Fluoride adsorption onto the synthesized sample was investigated using batch adsorption method. The experimental parameters chosen for adsorption studies were: pH (3.0-10.0), temperature (35-55°C), concentrations of adsorbent (0.5-3.0 g/L), adsorbate (10-100 mg/L) and some anions. Adsorption of fluoride onto mixed iron oxide was initially very fast followed by a slow adsorption phase. By varying the initial pH in the range of 3.0-10.0, maximum adsorption was observed at a pH of 5.75. Presence of either SO(4)(2-) or Cl(-) adversely affected the adsorption of fluoride in the order of SO(4)(2-)>Cl(-). The FTIR studies of fluoride loaded adsorbent showed that partly the adsorption on the surface took place at surface hydroxyl sites. Mössbauer studies indicated that the overall absorption had gone down after fluoride adsorption that implies it has reduced the crystalline bond strength. The relative absorption area of ferrihydrite was marginally increased from 14 to 17%.