Large photoconductivity of oxygen-deficient La(0.7)Ca(0.3)MnO(3)/SrTiO(3) heterostructures

The electrical resistance of stoichiometric and oxygen-deficient epitaxial 10 nm thick La(0.7)Ca(0.3)MnO(3) thin films on SrTiO(3) under photoexcitation covering the visible to the ultraviolet range has been investigated systematically as a function of illumination intensity, wavelength and temperature. In contrast to as-prepared films, the oxygen-deficient samples exhibit large photoconductivity of several orders of magnitude at low temperatures. By our detailed comparative analysis of the electrical conductivity of the film/substrate heterostructure and the bare substrate we are able to elucidate contributions of both carrier generation in the film and carrier injection from the substrate to the observed effect.