Wettability and surface composition of partly and fully regenerated cellulose thin films from trimethylsilyl
Tamilselvan Mohan1, Rupert Kargl, Aleš Doliška
1Laboratory for Characterization and Processing of Polymers, Faculty of Mechanical Engineering, University of Maribor, Smetanova 17, SI-2000 Maribor, Slovenia.
Abstract:
The wettability and surface free energy (SFE) of partly and fully regenerated cellulose model surfaces from spin coated trimethylsilyl cellulose were determined by static contact angle (SCA) measurements. In order to gain detailed insight into the desilylation reaction of the surfaces the results from SCA measurements were compared with data from other surface analytical methods, namely thickness measurements, X-ray photoelectron spectroscopy (XPS) and attenuated total reflectance infrared spectroscopy (ATR-IR). Additionally, the influence of ultra high vacuum treatment (UHV) during XPS measurements on the water wettability and surface morphology of regenerated cellulose thin films was investigated. The wetting of polar and non-polar liquids increased with prolonged regeneration time, which is reflected in the higher SFE values and polarities of the films. After UHV treatment the water SCA of partly regenerated films decreases, whereas fully regenerated cellulose shows a higher water SCA. Therefore it is assumed that volatile desilylation products tend to adsorb on partly regenerated films, which strongly influences their wettability.
More Related Videos
08:02Thin Film Composite Silicon Elastomers for Cell Culture and Skin Applications: Manufacturing and Characterization
Published on: July 3, 2018
07:25Green and Low-cost Production of Thermally Stable and Carboxylated Cellulose Nanocrystals and Nanofibrils Using Highly Recyclable Dicarboxylic Acids
Published on: January 9, 2017