Shear bond strength of rebonded brackets after removal of adhesives with Er,Cr:YSGG laser

This study was conducted to examine the bond strength of rebonded orthodontic brackets after adhesive residuals on the surface of the bracket bases were removed by Er,Cr:YSGG lasers. Seventy-six brackets bonded to premolars with a self-etching primer adhesive system were equally divided into four groups after the first debonding with the bracket bases (Group 1) untreated, and treated by (Group 2) Er,Cr:YSGG laser, (Group 3) sandblaster, and (Group 4) Er,Cr:YSGG laser/sandblaster. The treated brackets were rebonded to the new premolars in the same manner as the first-stage experiment. The shear bond strengths were measured, with the bonding/debonding procedures repeated once after the first debonding, and the bracket/adhesive failure modes were evaluated after each debonding. The treated bracket base surfaces were observed under a scanning electron microscopy (SEM). The mean rebond strengths were significantly lower in group 1 than in other groups, and there were no significant differences between the other groups. The mean initial bond strength was significantly higher than the mean rebond strength in group 1 but there was no significant difference between the two in the other three groups. Failures at the bracket-adhesive interface occurred frequently at second debonding in group 1. Under the SEM, residual adhesive was removed from the bracket bases by Er,Cr:YSGG laser, while adhesive remnant was seen underneath the meshwork of the bracket bases and microroughness appeared on the meshwork after sandblasting. Er,Cr:YSGG laser certainly could serve the purpose of promoting the use of recycled orthodontic brackets.