Evaluation of spinal instrumentation rod bending characteristics for in-situ contouring

Bending characteristics were studied in rods used for spinal instrumentation at in-situ contouring conditions. Five groups of five 6 mm diameter rods made from: cobalt alloy (VITALLIUM), titanium-aluminum-vanadium alloy (SDI™), β-titanium alloy (TNTZ), cold worked stainless steel (STIFF), and annealed stainless steel (MALLEABLE) were studied. The bending procedure was similar to that typically applied for in-situ contouring in the operating room and included two bending cycles: first--bending to 21-24° under load with further release of loading for 10 min, and second--bending to 34-37° at the previously bent site and release of load for 10 min. Applied load, bending stiffness, and springback effect were studied. Statistical evaluation included ANOVA, correlation and regression analysis. TNTZ and SDI™ rods showed the highest (p < 0.05) springback at both bending cycles. VITALLIUM and STIFF rods showed mild springback (p < 0.05). The least (p < 0.05) springback was observed in the MALLEABLE rods. Springback significantly correlated with the bend angle under load (p < 0.001). To reach the necessary bend angle after unloading, over bending should be 37-40% of the required angle in TNTZ and SDI™ rods, 27-30% in VITALLIUM and STIFF rods, and around 20% in MALLEABLE rods.