Ferroelectric nanostructures fabricated by focused-ion-beam milling in epitaxial BiFeO3 thin films

We studied a suitable route to fabricate ferroelectric islands by focused-ion-beam milling in bismuth ferrite epitaxial thin films. Piezoresponse force microscopy shows that the damage induced by the milling process is extended to 1 µm away from the edge of the focused-ion-beam patterned islands. After a combined vacuum and oxygen atmosphere annealing procedure, ferroelectricity is fully recovered in structures with sizes down to 500 nm, while for 250 nm islands the defects at the interfaces induce polarization direction pinning.