Bisquinoxaline-fused porphyrins for dye-sensitized solar cells

5,10,15,20-Tetrakis(2,4,6-trimethylphenyl)-6'-carboxylquinoxalino[2,3-b]quinoxalino[12,13-b']porphyrinatozinc(II) (ZnPBQ) is synthesized to evaluate the effects of π elongation of quinoxaline-fused porphyrins on the optical, electrochemical, and photovoltaic properties. ZnPBQ showed an intensified Soret band as well as red-shifted Soret and Q bands relative to 5,10,15,20-tetrakis(2,4,6-trimethylphenyl)-6'-carboxylquinoxalino[2,3-b]porphyrinatozinc(II) (ZnPQ), demonstrating the improved light-harvesting property of ZnPBQ. The optical and electrochemical HOMO-LUMO gaps were consistent with those estimated by DFT calculations. The photovoltaic properties were compared under optimized conditions, in which a sealed device structure with TiCl(4) -treated, TiO(2) double layers was used. The ZnPBQ cell exhibited a relatively high power conversion efficiency (η) of 4.7%, which was smaller than that of the ZnPQ cell (η=6.3%). The weaker electronic coupling between the LUMO of ZnPBQ and conduction band (CB) of TiO(2) or more tilted geometry of ZnPBQ on the TiO(2) surface may result in the low electron injection/charge collection efficiency as well as the low incident photon-to-current efficiency (IPCE) for the ZnPBQ cell (maximum IPCE=56%) relative to the ZnPQ cell (maximum IPCE=75%), leading to the lower η value of the ZnPBQ cell than that of the ZnPQ cell. In addition, the open-circuit potential of the ZnPBQ cell also slightly decreased with the effect of charge recombination from the electrons injected into the CB of TiO(2) to I(3)(-).