The effect of sterilization methods on the physical properties of silk sericin scaffolds

Protein-based biomaterials respond differently to sterilization methods. Since protein is a complex structure, heat, or irradiation may result in the loss of its physical or biological properties. Recent investigations have shown that sericin, a degumming silk protein, can be successfully formed into a 3-D scaffolds after mixing with other polymers which can be applied in skin tissue engineering. The objective of this study was to investigate the effectiveness of ethanol, ethylene oxide (EtO) and gamma irradiation on the sterilization of sericin scaffolds. The influence of these sterilization methods on the physical properties such as pore size, scaffold dimensions, swelling and mechanical properties, as well as the amount of sericin released from sericin/polyvinyl alcohol/glycerin scaffolds, were also investigated. Ethanol treatment was ineffective for sericin scaffold sterilization whereas gamma irradiation was the most effective technique for scaffold sterilization. Moreover, ethanol also caused significant changes in pore size resulting from shrinkage of the scaffold. Gamma-irradiated samples exhibited the highest swelling property, but they also lost the greatest amount of weight after immersion for 24 h compared with scaffolds obtained from other sterilization methods. The results of the maximum stress test and Young's modulus showed that gamma-irradiated and ethanol-treated scaffolds are more flexible than the EtO-treated and untreated scaffolds. The amount of sericin released, which was related to its collagen promoting effect, was highest from the gamma-irradiated scaffold. The results of this study indicate that gamma irradiation should have the greatest potential for sterilizing sericin scaffolds for skin tissue engineering.