Flexible and semitransparent strain sensors based on micromolded Pd nanoparticle-carbon μ-stripes

Flexible resistive strain sensors have been fabricated by micromolding Pd alkanethiolate on polyimide substrates and subjecting to thermolysis in air. Thus produced stripes were ∼1 μm wide with spacing of ∼0.5 μm and contained Pd nanoparticles in carbon matrix. The nanoparticle size and the nature of carbon are much dependent on the thermolysis temperature as is also the resistance of the microstripes. Generally, lower thermolysis temperatures (<230 °C) produced stripes containing small Pd nanoparticles with significant fraction of carbon from the precursor decomposition. The stripes were poorly conducting yet interestingly, exhibited change of resistance under tensile and compressive strain. Particularly noteworthy are the stripes produced from 195 °C thermolysis, which showed a high gauge factor of ∼390 with strain sensitivity, 0.09%. With molding at 230 °C, the stripes obtained were highly conducting, and amazingly did not change the resistance with strain even after several bending cycles. The latter are ideal as flexible conduits and interconnects. Thus, the article reports a method of producing flexible sensitive strain sensors on one hand and on the other, flexible conduits with unchanging resistance, merely by fine-tuning the precursor decomposition under the molding conditions.