[Preparation and ectopic osteoinduction study of macroporous bone substitute with calcium phosphate cements and...

To prepare macroporous bone substitute composed of calcium phosphate cements and rhBMP-2 loaded gelatin microspheres, and to investigate ectopic osteoinduction of the composite.

After being prepared by improved emulsified cold-condensation method and crosslinked by 5% genipin solution,gelatin microspheres (GMs) were observed by scanning electron microscope (SEM) and loaded with rhBMP-2 by adsorption. Macroporous bone substitute was developed by mixing calcium phosphate cement (CPC) with 2.5% GMs, being as the experimental group,and CPC with rhBMP-2 was the control group. After the both composites had been soaked in the sodium chloride for 1 week or 3 weeks, compressive strength of the composites were tested, and the cross-sections were observed by SEM. Concentrations of rhBMP-2 in the solutions at different time by ELISA method and the cumulative drug release amount was calculated. The composites had been implanted in the muscle bags of the mouses for 3 weeks. Then the tissues around the materials were collected, stained by hematoxylin and eosin, and Ca and ALP in the tissues were also measured.

Gelatin microspheres were spherical with diameters of (62 +/- 18) microm. Macropores appeared in the experimental materials 1 week and 3 weeks after being soaked,and total porosity, macroporosity, cumulative release amount of rhBMP-2 in the experimental group were higher than that in the control. But compressive strength of the experimental group was lower than that of the control group 3 weeks after being soaked. Results of HE stain showed chondral formation in both groups, but there were more chondral tissues in the experiment group, and so were the concentrations of Ca and ALP.

Macroporous calcium phosphate cement can be prepared by using rhBMP-2 loaded gelatin microspheres, and it is an excellent bone substitute due to it's proterty of promoting rhBMP release and powerful ectopic osteoinduction.